DATA SHEET AISI 310S

Stainless steels which – beside the necessary percentage of Chromium – contain a good amount of Nickel and possibly of Molybdenum.

REQUEST INFORMATION
* The values indicated in the tables are approximate and non-binding.
acciai austenitic GO TO PRODUCTS SECTION
for thicknesses and formats available

ALTERNATIVE NAMES

ASTM EN UNS JIS
310S 1.4845 S31008 SUS 310S

CHEMICAL COMPOSITION

310S Chemical Composition - Maximum Value
C Mn Si Cr Ni P Mo Other
0.1 - 1.0 22-24 19-22 0.045 2-2.25/td> N<0.11
Typical Value
0.08 0 0 22 20.4 0

MECHANICAL CHARACTERISTICS

Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness
Rockwell B (HR B) max Brinell (HB) max
520
(580)
205
(270)
40 95 220

END USES

AISI 310S steel is used when the end products must withstand very high temperatures. Thanks to extremely high Nickel and Chromium content (even higher than those in AISI 309S) this steel is highly resistant to corrosion at high temperatures, up to 1100 degrees in oxidising environments and up to 1000 degrees in highly reducing environments.

AISI 310S is austenitic steel which cannot be tempered and is characterised not to be magnetic in annealed or cold machining state. Typical applications are pipes and boxes for annealing. Boxes for nitriding gas turbine parts and reaction engines, parts for ovens with continuous passage.